產(chǎn)品&供應尺寸 |
| |
|
Products &
Size(mm)
|
AISI
Grade
|
Chemical Composition
|
DIN
|
|
C
|
Si
|
Mn
|
Ni
|
Cr
|
Mo
|
V
|
W
|
Co
|
High Speed Steel
11  ?230 |
M 1
|
0.84
|
0.4
|
0.3
|
|
3.9
|
8.6
|
1.2
|
1.75
|
|
1.3346
|
|
M 2
|
0.86
|
0.3
|
0.3
|
|
3.9
|
4.85
|
1.85
|
6.15
|
|
1.3343
|
|
M 4
|
1.35
|
0.3
|
0.3
|
|
4.1
|
5
|
4
|
6
|
|
|
|
M 7
|
1.02
|
0.4
|
0.3
|
|
3.75
|
8.65
|
1.95
|
1.75
|
|
1.3348
|
|
M 35
|
0.93
|
0.35
|
0.3
|
|
3.95
|
4.85
|
1.8
|
6.1
|
4.65
|
1.3243
|
|
M 42
|
1.08
|
0.5
|
0.3
|
|
3.85
|
9.25
|
1.17
|
1.45
|
7.85
|
1.3247
|
|
M 50
|
0.84
|
0.5
|
0.25
|
|
4.1
|
4.25
|
1
|
|
|
1.3551
|
|
T 1
|
0.75
|
0.3
|
0.3
|
|
4.1
|
|
1.1
|
18
|
|
1.3355
|
Tool Steel
15 ?580 |
A 2
|
0.98
|
0.25
|
0.55
|
|
4.9
|
1
|
0.2
|
|
|
1.2363
|
|
A 8
|
0.55
|
0.9
|
0.35
|
|
5
|
1.3
|
1.2
|
1.2
|
|
|
|
A 9
|
0.51
|
1
|
0.3
|
1.45
|
5
|
1.4
|
0.95
|
|
|
|
|
D 2
|
1.54
|
0.3
|
0.35
|
|
11.5
|
0.75
|
0.7
|
|
|
1.2379
|
|
H 10
|
0.38
|
0.9
|
0.5
|
|
3.3
|
2
|
0.5
|
|
|
|
|
H 11
|
0.38
|
1.02
|
0.35
|
|
5.07
|
1.22
|
0.38
|
|
|
1.2343
|
|
H 12
|
0.35
|
1.05
|
0.4
|
|
5.25
|
1.4
|
0.3
|
1.3
|
|
1.2606
|
|
H 13
|
0.39
|
1.02
|
0.35
|
|
5.1
|
1.3
|
1
|
|
|
1.2344
|
|
|
0.38
|
0.4
|
0.4
|
|
5
|
3.1
|
0.5
|
|
|
1.2367
|
|
O 1
|
0.9
|
0.2
|
1.3
|
|
0.55
|
|
|
0.5
|
|
1.2510
|
|
S 1
|
0.45
|
0.9
|
0.3
|
|
1.05
|
0.3
|
0.18
|
1.9
|
|
|
|
S 7
|
0.49
|
0.32
|
0.67
|
|
3.25
|
1.46
|
0.26
|
|
|
|
Bearing Steel
15 ?580 |
52100
|
1.04
|
0.25
|
0.35
|
|
1.4
|
|
|
|
|
1.3505
|
Stainless Steel
15 ?450 |
304
|
0.06
|
0.35
|
1.7
|
8.5
|
18.2
|
|
|
|
|
1.4301
|
|
310 S
|
0.08
|
0.4
|
1.7
|
19.5
|
25
|
|
|
|
|
1.2782
|
|
316 L
|
0.02
|
0.45
|
1.6
|
10.5
|
16.2
|
2.15
|
|
|
|
1.4404
|
|
321
|
0.04
|
0.5
|
1.4
|
9.5
|
17.5
|
|
Ti% = 5 x %C min.
|
1.4878
|
|
403Cb+
|
0.15
|
0.4
|
0.6
|
0.5
|
10.8
|
0.85
|
0.22
|
Nb%=0.39
|
|
|
410
|
0.12
|
0.4
|
0.4
|
|
11.8
|
|
|
|
|
1.4006
|
|
416
|
0.13
|
0.4
|
1
|
0.4
|
12.2
|
|
S% > 0.15
|
|
|
|
420
|
0.27
|
0.4
|
0.4
|
|
12.4
|
|
|
|
|
1.4034
|
|
422
|
0.22
|
0.4
|
0.4
|
0.6
|
12
|
0.95
|
0.2
|
0.95
|
|
1.4923
|
|
431
|
0.17
|
0.4
|
0.65
|
1.6
|
15.7
|
|
|
|
|
1.4057
|
|
440 C
|
1.05
|
0.4
|
0.4
|
|
16.5
|
0.45
|
|
|
|
1.4125
|
|
GTD450
|
0.05
|
0.4
|
0.4
|
6.5
|
15
|
0.6
|
Cu%=1.5
Nb=0.37
|
|
|
630
|
0.02
|
0.33
|
0.66
|
4.85
|
15.3
|
Cu% = 3.4 Nb% = 0.24
|
17-4PH
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
特性: |
|
|
低氧化物,硫化物之高級清淨鋼 |
|
|
高均勻性 |
|
|
低偏析性(微觀) |
|
|
無巨觀偏析 |
|
|
晶粒細化 |
|
|
碳化物分布均勻,特別是高速鋼 |
|
|
機械性質(zhì)穩(wěn)定 |
|
|
鑄錠表面平整 |
|
機械性質(zhì): |
|
|
改善金屬之延展性 |
|
|
增加材料之橫向強度 |
|
|
鏡面鋼之優(yōu)良材料 |
|
|
加工性佳 |
|
|
耐高溫性佳 |
|
|
可焊接性佳 |
|
|
耐腐蝕性佳 |
|
|
熱作性佳 |
|
|
硬化處理時扭曲變形量低 |
|
|
| ESR級產(chǎn)品廣泛應用於IC封裝模、光學鏡片模、鋁擠型模、壓鑄模具、熱鍛模具、發(fā)動機葉片、極細線等各種高科技材料。 |
|
|